EPO-TEK® 323LP-LH Ultra
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8AFZxd_EPO-TEK-323LP-LH-Ultra.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Longer pot life version of EPO-TEK® 353ND designed for semiconductor, hybrid, fiber-optic, hard -disk drive and medical applications. This product easily meets halogen-free requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 27 | ppm | |
| K+ | 4 | ppm | |
| Na+ | 2 | ppm | |
| NH4+ | 519 | ppm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 413 | °C | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus | 2.67 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.48 | % | |
| 250°C | 0.71 | % | |
| 300°C | 1.2 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 117 | °C | |
| CLTE - Flow | |||
| -- 1 | 3.1E-5 | cm/cm/°C | |
| -- 2 | 1.3E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 3 | 1.570 | ||
| Transmittance | |||
| 640 to 800 nm | > 90.0 | % | |
| 820 to 1620 nm | > 94.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Clear/Transparent | ||
| -- 5 | Yellow | ||
| Density | |||
| Part B | 1.09 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 6(23°C) | 3.9 | Pa·s | |
| Curing Time (90°C) | 0.50 | hr | |
| Pot Life | 2100 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 88 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa |
| Note Message | |
|---|---|
| 1 . | Below Tg |
| 2 . | Above Tg |
| 3 . | 589 nm |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 240 NG4 Y2 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Evermore PUR UF-152 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| DEXFLEX® 711 | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| Greenflex® MP 35 F | Versalis S.p.A. | EVA | Greenflex® |
| LITEN MB 71 | UNIPETROL RPA | PE Homopolymer | LITEN |