ATTANE™ 4607GC
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 89pLch_ATTANE-4607GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer is a skin layer in cast film offers excellent low temperature hot tack properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer exhibits excellent stretchability as well as good physical and cling properties. ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer can also be utilised in blown film coextrusion where it is combined with other resins having excellent bubble stability allowing ATTANE™ 4607GC Ultra Low Density Ethylene/Hexene Copolymer to be used as a sealant in multilayer film structures. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.904 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Energy (23 µm) | 5.00 | J | Internal method |
| Film Puncture Force (23 µm) | 48.0 | N | Internal method |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm | 4.30 | MPa | ISO 527-3 |
| TD : Yield, 23 µm | 3.60 | MPa | ISO 527-3 |
| MD : Break, 23 µm | 33.0 | MPa | ISO 527-3 |
| TD : Break, 23 µm | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm | 500 | % | ISO 527-3 |
| TD : Break, 23 µm | 630 | % | ISO 527-3 |
| Dart Drop Impact (23 µm) | 180 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23 µm | 190 | g | ASTM D1922 |
| TD : 23 µm | 390 | g | ASTM D1922 |
| Unstretched bond | 130 | g | ASTM D4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 72.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm) | 92 | ASTM D2457 | |
| Haze (23.0 µm) | 0.70 | % | ASTM D1003 |
| Additional Information |
|---|
| 对于在 Lab Collin 生产线上采用 15 米/分冷却辊于 25°C 下生产的单层薄膜所测量的薄膜属性。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 260 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜挤出的制造条件： 熔体温度：190 - 260 °C 建议的厚度范围：10 - 60 µm 脱离速度：150 - 300 米/分 冷却辊温度：20 - 60 °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Uniflon UNILUB 15 | UNIFLON | PTFE | Uniflon |
| CALP 4300G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Fainplast PVC PH 50/AM-UV | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| HAIPLEN H50 C12 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Sylvin 8376-92UV Black 2101 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |