Epocast 169A-1 / Hardener 9646
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 89f0GC_Epocast-169A-1-Hardener-9646.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 169A-1 resin with 9646 Hardener epoxy syntactic is a low-density foam which cures at room temperature to a carvable, woodlike product. The epoxy syntactic has good dimensional stability under changing humidity conditions and is pourable for easier application as a core fill and honeycomb reinforcement. Epocast® 169A-1 resin can also be used with 9646-A Hardener at the same mix ratio, to produce a non-flow paste consistency. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.560 | g/cm³ | ASTM D1622 |
| -- 2 | 0.700 | g/cm³ | ASTM D1622 |
| -- 3 | 0.960 | g/cm³ | ASTM D1622 |
| Viscosity | ASTM D2196 | ||
| 25°C 4 | Paste | ASTM D2196 | |
| 25°C 5 | Pourable | ASTM D2196 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 50 gms (25°C) 6 | 30.0 - 50.0 | min | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Lap Shear - AL/AL | 15.4 | MPa | ASTM D1002 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 593 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| 25°C 7 | 51.7 | MPa | ASTM D695 |
| 25°C 8 | 18.6 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 35 | ||
| Thermoset Mix Viscosity 9(25°C) | 350 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 24 hours at 75°F ± 5°F (24°C ± 2°C), or room temperature gel plus 2 hours at 150°F ± 10°F (66°C ± 5°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | Resin |
| 5 . | System |
| 6 . | System |
| 7 . | Ultimate |
| 8 . | Yield |
| 9 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT3080-729UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Mylar® A (142 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| FRAGOM LC/3013 RR | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Innothane® IE-72DC | Innovative Polymers, Inc. | TSU | Innothane® |
| LUVOCOM® 1301-8836 | Lehmann & Voss & Co. | PPS, Linear | LUVOCOM® |