SABIC® LDPE PCG81
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 89SnY9_SABICLDPEPCG81.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low density polyethylene for Healthcare Description SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG81 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Blow Fill Seal, Blow Molding and Blown Film to produce ampoules, bottles, but also intermediate packaging (bags) for active pharmaceutical ingredients and secondary packaging. Compliance to Regulations SABIC® LDPE PCG81 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 170 | MPa | ISO 527-3 |
| TD | 170 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 11.0 | MPa | ISO 527-3 |
| TD : Yield | 11.0 | MPa | ISO 527-3 |
| MD : Fracture | 25.0 | MPa | ISO 527-3 |
| TD : Fracture | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | > 200 | % | ISO 527-3 |
| TD : Fracture | > 500 | % | ISO 527-3 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD | 55000 | N | ISO 6383-2 |
| TD | 45000 | N | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | 220 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 50 | g | Internal method |
| Re-blocking | g | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 109 | °C | DIN 53765 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 68 | ASTM D2457 | |
| Clarity | 15.0 | Internal method | |
| Haze | 6.0 | % | ASTM D1003A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MOSTEN TB 002 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Ultramid® 8262G HS BK-125 | BASF Corporation | Nylon 6 | Ultramid® |
| Globalene® STM866 | Lee Chang Yung Chemical Industry Corp. | PP, Unspecified | Globalene® |
| INEOS PP R55C-00 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |
| LUVOCOM® 19/CF/30 | LEHVOSS Group | Nylon 46 | LUVOCOM® |