Alcryn® 2180 BK Datasheet,MPR,Advanced Polymer Alloys-SHANGHAI SUSHENG

Message
Alcryn®2180 BK is a melt processable rubber (MPR) material,. This product is available in North America, Europe or Asia Pacific,. Alcryn®The main features of 2180 BK are: Comply with WEEE standard ROHS certification high liquidity Good tear strength chemical resistance Typical application areas include: Wire and cable Automotive Industry Hose engineering/industrial accessories Sealing applications

General Information
Features	High Friction Good tear strength Good wear resistance High liquidity Good chemical resistance
Uses	Handle Cable sheath Wire sheath Washer Pipe Pipe fittings Seals Weather-resistant sealing strip Car interior parts
Agency Ratings	EU 2002/96/EC (WEEE)
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.30	g/cm³	ASTM D792, ISO 1183

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 1.90 mm, Compression Molded)	78		ASTM D2240, ISO 868

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress
100% strain	4.10	MPa	ASTM D412
100% strain, 1.90mm	4.10	MPa	ISO 37
Tensile Strength (Break, 1.90 mm)	12.5	MPa	ASTM D412, ISO 37
Tensile Elongation
Fracture	550	%	ASTM D412
Fracture, 1.90mm	550	%	ISO 37
Tear Strength ¹(24°C)	61.0	kN/m	ASTM D624
Compression Set			ASTM D395, ISO 815
24°C, 22 hr	22	%	ASTM D395, ISO 815
100°C, 22 hr	88	%	ASTM D395, ISO 815

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-50.0	°C	ASTM D746, ISO 812

Additional Information
The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.The value listed as Density, ISO 1183, was tested in accordance with ISO 2781.The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48.Permanent Set (Tension), ASTM D412, Compression Molding, 1.9 mm: 17%100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 148%Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 112%Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 1106%Hardness, ISO 48, Physical Retention After 7 Days at 125°C, Shore A, Compression Molding, 1.9 mm: 77Viscosity, ASTM D3835, 300 s-1 at 190°C, Compression Molding, 1.9 mm: 430 Pa*sTypical Processing Temperature, Compression Molding, 1.9 mm: 177° CVolume Change, ASTM D471, ISO 1817, After 7 days, 100°C, Water, Compression Molding, 1.9 mm: 12%Volume Change, After 7 days,ASTM D471, ISO 1817, 24°C, Fuel B, Compression Molding, 1.9 mm: 26%Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, ASTM #1 Oil, Compression Molding, 1.9 mm: -6%Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, IRM 903 Oil #3, Compression Molding, 1.9 mm: 16%Clash-Berg Stiffness Temperature, ASTM D1043, 10000 psi, Compression Molding, 1.9 mm: -19° C

Additional Information

The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.The value listed as Density, ISO 1183, was tested in accordance with ISO 2781.The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48.Permanent Set (Tension), ASTM D412, Compression Molding, 1.9 mm: 17%100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 148%Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 112%Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 1106%Hardness, ISO 48, Physical Retention After 7 Days at 125°C, Shore A, Compression Molding, 1.9 mm: 77Viscosity, ASTM D3835, 300 s-1 at 190°C, Compression Molding, 1.9 mm: 430 Pa*sTypical Processing Temperature, Compression Molding, 1.9 mm: 177° CVolume Change, ASTM D471, ISO 1817, After 7 days, 100°C, Water, Compression Molding, 1.9 mm: 12%Volume Change, After 7 days,ASTM D471, ISO 1817, 24°C, Fuel B, Compression Molding, 1.9 mm: 26%Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, ASTM #1 Oil, Compression Molding, 1.9 mm: -6%Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, IRM 903 Oil #3, Compression Molding, 1.9 mm: 16%Clash-Berg Stiffness Temperature, ASTM D1043, 10000 psi, Compression Molding, 1.9 mm: -19° C

Note Message
1 .	C mould

Category:	MPR , Melt Processable Rubber
Manufacturer:	Advanced Polymer Alloys
Trademark:	Alcryn®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	899SKu_Alcryn-2180-BK.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Salflex 364A	Salflex Polymers Ltd.	TPV	Salflex
Daplen™ EF005AE	Borealis AG	PP, Unspecified	Daplen™
ICORENE® 9104 GW1 Natural 0000	ICO Polymers EMEA, A Division of A. Schulman	LLDPE	ICORENE®
Jiangsu Sinarise ZM788	Jiangsu Sinarise New Material Technology Co., Ltd	TPE	Jiangsu Sinarise
Sylvin 6920X08 Grey 9550	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin