QR Resin QR-1018IM-FR
| Category: | PC , Polycarbonate |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 894oz3_QR-Resin-QR-1018IM-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Available with UV (V) or Release (R). Flame Packages Available (0.0625 in min. thickness): 94V-2, 94V-0, 94-5VA |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus | 2230 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -29°C | 430 | J/m | |
| 23°C | 640 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 132 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Rear Temperature | 260 to 282 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 282 to 304 | °C | |
| Nozzle Temperature | 277 to 299 | °C | |
| Processing (Melt) Temp | 282 to 299 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 2630 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Spartech Polycom PP5325 | Spartech Polycom | PP Homopolymer | Spartech |
| Sumiflex® K K761B | Mitsubishi Chemical Corporation | PVC Elastomer | Sumiflex® K |
| LNP™ STAT-KON™ RE004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Sylvin 9067-80 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |