Telcar® TELC-87-L832-A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 88kORs_Telcar-TELC-87-L832-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TELC-87-L832-A is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Telcar®The typical application fields of TELC-87-L832-A are: wire and cable |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.883 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain | 2.76 | MPa | ASTM D412 |
| Flow : 100% strain | 3.83 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture | 5.80 | MPa | ASTM D412 |
| Flow : Fracture | 5.80 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture | 540 | % | ASTM D412 |
| Flow : Fracture | 320 | % | ASTM D412 |
| Tear Strength - Across Flow | 36.9 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 28 | % | ASTM D395 |
| 70°C, 22 hr | 58 | % | ASTM D395 |
| 90°C, 70 hr | 68 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (136°C, 168 hr) | 50 | % | ASTM D412 |
| Change in Ultimate Elongation (136°C, 168 hr) | -10 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (23°C, 1 kHz) | 2.24 | ASTM D150 |
| Additional Information |
|---|
| 变形 T2/T1 - 150C, ，2000 GMS (UL-15841) = 0.54紫外线稳定性= 是 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E390 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Thermoset Plastics 310 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| UBE Nylon 5034 TX18 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Boda BDP-H9701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| LNP™ LUBRICOMP™ KA000 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |