INNOPOL® PP CS 1-3830 MV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 88foeg_INNOPOL-PP-CS-1-3830-MV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-3830 MV is a 30 % glass fiber filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-3830 MV is recommended for producing injection molded products, where the required properties are excellent strength and stiffness besides high heat stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 86.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 157 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 | |
| flammability- Automotive materials (thickness d > 1 mm) | + | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 190 - 240 | °C | |
| Front Temperature | 190 - 240 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPSTAT F 10C 05 V0 28 | Vamp Tech | PPS | VAMPSTAT |
| Next Nylon 66 Prime Series PG33-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Hangzhou Keli ACS C-240 | Hangzhou Keli Chemical Co., Ltd. | ACS | Hangzhou Keli ACS |
| OnForce™ LFT PP-50LGF/001 Natural | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| Orgalloy® LE 60HM | Arkema | Nylon 6 Alloy | Orgalloy® |