TORZEN Marathon™ FRU4800XHL BK01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN Marathon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 88CkgI_TORZEN-Marathon-FRU4800XHL-BK01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN Marathon™ FRU4800XHL BK01 is a flame retardant, heat stabilized black Polyamide 66 resin suitable for injection molding. It does not contain elemental bromine, phosphorus or heavy metals. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.3 to 1.6 | % | |
| Flow : 2.00 mm | 1.3 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 13 | % | ISO 527-2 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Melting Temperature | 263 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) (3.00 mm) | 600 | V | UL 746 |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 0 | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.400 mm | V-0 | ||
| 0.800 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.400 mm | 960 | °C | |
| 0.800 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | 990 | °C | |
| 0.800 mm | 990 | °C | |
| 1.50 mm | 990 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Nozzle Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Screw Speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® POM 770/1.1 CF20 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| ExxonMobil™ LDPE LD 200.48 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Drystar™ 0831 | Eastman Chemical Company | Copolyester | Drystar™ |
| GAPEX® APP40GR17HB-NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| LNP™ COLORCOMP™ PX99848 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ COLORCOMP™ |