Next Nylon 66 Prime Series PXHS-01NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 86guM7_Next-Nylon-66-Prime-Series-PXHS-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 UnFilled Heat Stabilized Natural Compound Product Applications This grade is used for connector, Pin of automobile, Power steering reservoir tank, switch, canister, fuel filler tube etc Benefits Offering an excellent long -term heat stability and productivity |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.4 | -- | % | |
| Across Flow | 1.4 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.6 | -- | % | |
| Saturation 1 | 8.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 79 | -- | ||
| R-Scale | 115 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 80.0 | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | > 50 | % | ASTM D638 |
| Flexural Modulus | 3150 | 2900 | MPa | ASTM D790 |
| Flexural Strength | 110 | 75.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | 88 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 200 | -- | °C | |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | |
| Melting Temperature | 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 280 to 285 | °C | |
| Front Temperature | 285 to 290 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 TFE 13 SI 2 | RTP Company | PBT | RTP |
| Shandong PP PQ01 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Norfor® 130 GF/10 NATURALE | SO.F.TER. SPA | PPE | Norfor® |
| Hifax ETA3183 | LyondellBasell Industries | TPO (POE) | Hifax |
| Karina MBPEB WHITE 1000/5035-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |