LNP™ THERMOCOMP™ 9X10312 compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8650YE_LNP-THERMOCOMP-9X10312-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 9X10312 is 50% glass fiber reinforced, impact modified nylon material. High modulus, high flow and good ductility, Low Moisture Absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.12 | % | |
| Across Flow : 3.20 mm | 0.44 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 15000 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 212 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus | 13000 | MPa | ASTM D790 |
| Flexural Strength | 310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 12.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 250 | °C | ASTM D648 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 4.00 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 0.010 | ASTM ES7-83 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 80*10*3 sp=62mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® LDS 3730 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® LDS |
| Nypol® PA A3 G30 HS UV RH AMLA144 NR450 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| EPO-TEK® H37-MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hiprolon® 11 ESNWHL P20 | Arkema | Nylon 1012 | Hiprolon® |
| LNP™ THERMOCOMP™ DF006ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |