Starex VE-0856 U
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 85Yced_StarexVE0856U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex VE-0856 U is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Starex VE-0856 U's application areas include electrical appliances and commercial/office supplies. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.6 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.36 - 0.44 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.38 - 0.47 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.38 - 0.47 | % | ISO 2577 |
| Traffic : 3.20mm | 0.36 - 0.44 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 95 | ASTM D785 | |
| R scale | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 27.0 | MPa | ASTM D638 |
| Fracture | 28.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 13 | % | ASTM D638 |
| Fracture | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 56.0 | MPa | ASTM D790 |
| -- 8 | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 23 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 200 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 160 | J/m | ASTM D256 |
| 23°C 10 | 21 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 84.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 72.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 2.0 mm | V-0 5VB | UL 94 | |
| 2.5 mm | V-0 5VB | UL 94 | |
| 3.0 mm | V-0 5VB 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 210 - 220 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 147 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex MP-0670 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| TAFMER™ A-20090 | Mitsui Chemicals America, Inc. | PAO | TAFMER™ |
| Nypol® PA A3 T40 HS NTLA013 NR327 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| DIOSHY® TPEE E955D-HD | DIOSHY Co.,Ltd. | TPEE | DIOSHY® |
| Sylvin 4299-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |