Halene H R5801
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 85UFNT_Halene-H-R5801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
R5801 is a HDPE grade for stretched tape / raffia application produced by the Mitsui CX Technology. This grade can be used for stretched tape / raffia for woven sacks and tarpaulin. R5801 is characterized by excellent processability and high mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, molding | 28.0 | MPa | ASTM D638 |
| Fracture, molding | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | > 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 250 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 240 | °C | |
| Cylinder Zone 2 Temp. | 200 - 240 | °C | |
| Cylinder Zone 3 Temp. | 200 - 240 | °C | |
| Cylinder Zone 4 Temp. | 200 - 240 | °C | |
| Cylinder Zone 5 Temp. | 200 - 240 | °C | |
| Die Temperature | 220 - 240 | °C |
| Extrusion instructions |
|---|
| Quench Temperature: 25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 CF 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| ARLEN™ C230 | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |
| Clariant Nylon 6/6 PA-113CF30 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LUVOCOM® 1880-8748 | Lehmann & Voss & Co. | LCP | LUVOCOM® |
| Polyrocks 3001APG30 | Polyrocks Chemical Co., Ltd | PBT | Polyrocks |