VALOX™ 364 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 85RkiG_VALOX-364-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Designed for outdoor telecommunications enclosure applications. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.80 to 1.0 | % | |
| Across Flow : 3.20 mm | 0.80 to 1.0 | % | |
| Outdoor Suitability | f2 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 46.9 | MPa | |
| Break | 40.0 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 70 | % | |
| Flexural Modulus 3(50.0 mm Span) | 1860 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 66.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 430 | J/m | |
| -20°C | 690 | J/m | |
| 23°C | 750 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Total Energy | 47.5 | J | |
| -20°C, Total Energy | 44.7 | J | |
| 23°C, Total Energy | 45.2 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 103 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 68.3 | °C | |
| Vicat Softening Temperature | |||
| -- | 115 | °C | ASTM D1525 5 |
| -- | 122 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 9.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance 6 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RX® 852 | Sumitomo Bakelite North America, Inc. | Phenolic | RX® |
| Next Nylon 66 Prime Series PXR-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| CompaDur® 121 GF 30 natural (005) | DimeLika Plast GmbH | PBT | CompaDur® |
| LNP™ LUBRICOMP™ FL004 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| EPAMOULD 260A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |