Nucrel® 0910
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Nucrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 83VhDl_Nucrel-0910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nucrel® 0910 is a copolymer of ethylene and methacrylic acid, made with nominally 9 wt% methacrylic acid. The resin is available for use in conventional extrusion and coextrusion equipment. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 8.7 | wt% |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.0 | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 100 | °C | DSC, ISO 3146 |
| Freezing Point | |||
| -- | 82 | °C | ISO 3146 |
| -- | 82 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 2 Temp. | 235 | °C | |
| Cylinder Zone 3 Temp. | 260 | °C | |
| Cylinder Zone 4 Temp. | 285 | °C | |
| Cylinder Zone 5 Temp. | 285 | °C | |
| Adapter Temperature | 285 | °C | |
| Melt Temperature | < 310 | °C | |
| Die Temperature | 285 | °C |
| Extrusion instructions |
|---|
| Processing conditions shown are for extrusion coating/lamination. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2010 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Tisakril® ABS UNR | Tisan | ABS | Tisakril® |
| Aaroprene® CFPP 2020 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| Sylvin 8280-65 White 1518 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen EP200R | PolyMirae | PP Impact Copolymer | Moplen |