Durethan® BKV 35 CX H2.0 900876
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 833Iwd_Durethan-BKV-35-CX-H2-0-900876.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 35 % glass fibers, injection molding, heat aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 2.00 mm 1 | 0.70 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.15 | -- | % | |
| Flow : 260°C, 2.00 mm 3 | 0.20 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.050 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 180 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10000 | -- | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 270 | -- | MPa | |
| 23°C 6 | 280 | -- | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | -- | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-100, GF35 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | -- | kJ/m² | |
| 23°C | 70 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 505 TFE 5 | RTP Company | SAN | RTP |
| PRL PC-G30-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| Varcum 29320 | Durez Corporation | Phenolic | Varcum |
| Expandable PS F11MB-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| GERMAMID 6 XSZ | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |