Tislamid® PA6 PA6 15 GFR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Tisan |
| Trademark: | Tislamid® PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 82VLg2_Tislamid-PA6-PA6-15-GFR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tislamid® PA6 PA6 15 GFR is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Africa & Middle East or Europe for injection molding. Primary attribute of Tislamid® PA6 PA6 15 GFR: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | % | ISO 62 |
| Ash Content | 15 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 120 | MPa | |
| Break | 115 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.8 | % | |
| Break | 3.6 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 215 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 210 | °C | ISO 306/B120 |
| Melting Temperature | 220 to 225 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3732B NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Haysite BMC 14200 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Karina IVORY PVC COMPOUND 105551-35/1-Y-IS-SD-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9600-95 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen EP400L | LyondellBasell Industries | PP Impact Copolymer | Moplen |