LIHAN® A601
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 81ucGt_LIHAN-A601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® A601 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.3 to 1.6 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 to 1.4 | -- | % | ISO 62 |
| Water Content | 7.0 to 8.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | 100 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 55.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | 60 | % | ISO 527-2 |
| Flexural Modulus | 2100 | 1000 | MPa | ISO 178 |
| Flexural Stress | 65.0 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 20 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| CLTE - Flow | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 20 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 255 to 290 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 264E4861310 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| ELASTOSIL® LR 3004/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Globalene® 6231-20 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| IROGRAN® A 85 P 5350 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LG SBS LG-501 | LG Chem Ltd. | SBS | LG SBS |