LNP™ STAT-LOY™ 9X03508 compound
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 81bNaY_LNP-STAT-LOY-9X03508-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact. Also known as: LNP* STAT-LOY* Compound PDX-03508 Product reorder name: 9X03508 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (24 hr, 50% RH) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4830 | MPa | ASTM D638 |
| -- | 4470 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.1 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2 |
| Break | 53.1 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.1 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2 |
| Break | 2.2 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.7 | MPa | ASTM D790 |
| -- | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.00 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 230 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 218 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 186 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 179 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 199 to 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 TFE 15 | RTP Company | Nylon 66 | RTP |
| Tenopom® POM A3 MF PRTA010 PR304 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Homopolymer | Tenopom® POM |
| Ebalta GM 714 / PUR 4 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| ICORENE® 9042 | ICO Polymers APAC, A Division of A. Schulman | LMDPE | ICORENE® |
| Silastic® Q7-4565 | Dow Corning Corporation | Silicone | Silastic® |