AKROMID® A3 GF 30 natural (2397)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 81M8b9_AKROMID-A3-GF-30-natural-2397-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 30 natural (2397) is a 30% glass fibre reinforced polyamide 6.6 with high rigidity and strength and light inherent color Applications are mainly components in mechanical engineering |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 83.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption (Saturation, 23°C) | 5.2 to 5.8 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.9 to 2.1 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 130 to 150 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 160 to 175 | -- | °C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 240 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | > 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8800 | 7200 | MPa | ISO 178 |
| Flexural Stress 2 | 285 | 220 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 12 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 85 | 95 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 210 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.9E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 9.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 425 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Sinpolene HFR8224 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Styrolution PS 2600/2601 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| ELASTOSIL® LR 3071/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Deprene 251-60 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |