Hanwha Total PE 310A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 80n25R_Hanwha-Total-PE-310A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 310A is a low-density polyethylene resins for greenhouse films. This grade is designed to be processed in conventional blown film equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 15.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 740 | % | ASTM D638 |
| Coefficient of Friction | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm | 19.6 | MPa | ASTM D882 |
| TD : Break, 50 µm | 18.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 400 | % | ASTM D882 |
| TD : Break, 50 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 120 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 89.0 | °C | ASTM D1525 1 |
| Melting Temperature | 109 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Blocking, SAMSUNG TOTAL: 300 g/10cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 - 180 | °C | |
| Cylinder Zone 2 Temp. | 150 - 180 | °C | |
| Cylinder Zone 3 Temp. | 150 - 180 | °C | |
| Cylinder Zone 4 Temp. | 150 - 180 | °C | |
| Cylinder Zone 5 Temp. | 150 - 180 | °C | |
| Die Temperature | 150 - 170 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1 to 2.5 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-3357E | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Nanjing Hongrui PC CS1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| Next Nylon 66 Prime Series PGHSLR33-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| NYCOA Polyamide 7550 Nat | Nycoa (Nylon Corporation of America) | Nylon 12 | NYCOA Polyamide |
| Sylvin 8393-93C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |