LNP™ STAT-LOY™ YX02589C compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 80YAXy_LNPSTATLOYYX02589Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-LOY* YX02589C is a compound based on Polyester Elastomer resin containing proprietary fillers. Added features of this grade include: Antistatic, Clean Compounding System Also known as: LNP* STAT-LOY* Compound PDX-Y-02589 CCS Product reorder name: YX02589C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.61 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.65 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 5.5 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 8.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 38.0 | MPa | ASTM D638 |
| -- | 46.0 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 6.00 | MPa | ASTM D638 |
| Yield | 6.00 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 71 | % | ASTM D638 |
| Yield | 160 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 45.0 | MPa | ASTM D790 |
| -- 5 | 49.0 | MPa | ISO 178 |
| Flexural Stress | 2.36 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 18.1 | J | ASTM D3763 |
| -- | 25.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.5E-4 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 2.9E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 1.0E+13 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 - 193 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 227 - 238 | °C | |
| Processing (Melt) Temp | 216 - 238 | °C | |
| Mold Temperature | 27 - 54 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN5002SF | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| NEFTEKHIM PE 6748F (486H6) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Boltaron 4125 | Boltaron Performance Products | CPVC | Boltaron |
| ExxonMobil™ LDPE LD 506.07 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| POLYfill PPHC TS25020 | Polykemi AB | PP, Unspecified | POLYfill |