Eraclene® ML 70 U
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 80396w_Eraclene-ML-70-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene ML 70 U is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection moulding application. Its narrow molecular weight distribution leads to high mechanical properties (rigidity, impact strength) together with high stress cracking resistance. Main Application Eraclene ML 70 U is suggested to produce items with high mechanical performances, industrial containers, pallets and lids for open drums. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.8 | g/10 min | |
| 190°C/5.0 kg | 8.0 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 25.0 | MPa | |
| Break, Compression Molded | 20.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | 800 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 200 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| Melting Temperature | 135 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 220 to 275 | °C | |
| Middle Temperature | 220 to 275 | °C | |
| Front Temperature | 220 to 275 | °C | |
| Mold Temperature | 10.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® MN71120 | LyondellBasell Industries | LDPE | Microthene® |
| AVP™ TLL40CP | SABIC Innovative Plastics | PC | AVP™ |
| Iupilon® MB6002UR | Mitsubishi Engineering-Plastics Corp | PC+Acrylic | Iupilon® |
| LUVOCOM® 1100-7721/WT9016 | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| Vydyne® R535H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |