Aristech Altair® I-300
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7zlmhD_Aristech-Altair-I-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Altair® I-300 is a partially "cross-linked" commercial continuous cast acrylic sheet with unparalleled thermoforming properties. Aristech Acrylics LLC Altair® I-300 was developed for plumbingware, spa, automotive and other applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation, 3.18 mm) | 0.33 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 3.18 mm) | 90 to 100 | ASTM D785 | |
| Barcol Hardness (3.18 mm) | 48 to 52 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 3170 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.18 mm) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 5.5 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 3100 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (3.18 mm) | 246 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability 2(180°C, 3.18 mm) | No degradation | ASTM D4802 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance 3(250 to 370 nm) | < 1.0 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature (3.18 mm) | 171 to 193 | °C | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 21 | J/m | ASTM D256A |
| Instrumented Dart Impact 4(3.18 mm) | 4.07 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 87.8 | °C | ASTM D648 |
| CLTE - Flow (3.18 mm) | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat 5 | 1460 | J/kg/°C | ASTM C351 |
| Thermal Conductivity 6 | 0.20 | W/m/K | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 7 | 1.490 | ASTM D542 | |
| Transmittance | ASTM D1003 | ||
| 3180 µm 8 | 93.0 | % | |
| 3180 µm 9 | 93.0 | % | |
| Haze | ASTM D1003 | ||
| 3180 µm 10 | 1.0 | % | |
| 3180 µm 11 | 0.80 | % | |
| Yellowness Index 12(3.18 mm) | 0.45 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 0.125 in |
| 2 . | 30 min |
| 3 . | UV Spectrophotometer |
| 4 . | FTMS 406-M-1074 |
| 5 . | 0.125 in |
| 6 . | 0.125 in |
| 7 . | 0.125 in, Unaged |
| 8 . | Aged |
| 9 . | Unaged |
| 10 . | Aged |
| 11 . | Unaged |
| 12 . | Aged |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 CFGV 15/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| APEX® 90-A471R-65-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Elastron® D P.D100.A72.N | Elastron USA, Inc. | SBS | Elastron® D |
| Karina CLEAR PVC COMPOUND 80/275-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PB306G6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |