Next Nylon 66 Prime Series PGHS13-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7zNfl4_Next-Nylon-66-Prime-Series-PGHS13-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Heat Stabilized Black Compound Product Applications Under bonnet Automotive parts such as various covers & industrial Application. Benefits Very good rigidity at high temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.22 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.60 | -- | % | ASTM D955 |
| Transverse flow | 1.2 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.0 | -- | % | ASTM D570 |
| Saturation 1 | 7.1 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 85 | -- | ASTM D785 | |
| Class r | 113 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5100 | 3900 | MPa | ASTM D638 |
| Tensile Strength | 120 | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4800 | 3600 | MPa | ASTM D790 |
| Flexural Strength | 165 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 258 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 242 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 24 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-MFC-G20 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| SUNFROST® KD90EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| CP PRYME® Polypropylene PPC100NB-10M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Geon™ Vinyl Flexible R999A Black | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| PermaStat® 801 | RTP Company | Acetal (POM) Copolymer | PermaStat® |