Chemlon® 212 H is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 212 H are:
Typical application of Chemlon® 212 H: Automotive |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 to 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 79.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break, 23°C | 50 | % | |
| Flexural Modulus (23°C) | 2860 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 185 | °C | |
| 1.8 MPa, Unannealed | 92.2 | °C | |
| Melting Temperature | 216 | °C | |
| CLTE - Flow | 6.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 14 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | V-2 | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 218 to 235 | °C | |
| Middle Temperature | 229 to 252 | °C | |
| Front Temperature | 241 to 260 | °C | |
| Nozzle Temperature | 241 to 266 | °C | |
| Processing (Melt) Temp | 241 to 266 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PQ 83 T 10 | Plastcom | PP+EPDM | SLOVALEN® |
| VITAMIDE® BR16BL6093 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| ALCUDIA® EBA PA-1240 | REPSOL | EBA | ALCUDIA® EBA |
| DESLOY™ DSC891C | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| Hanwha Total PE R903U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |