LNP™ VERTON™ RVL29XXP compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7yEQ4a_LNP-VERTON-RVL29XXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RVL29XXP is a compound based on PA 66 resin, containing Long Glass Fiber, PTFE. Added features include; Internally Lubricated. Also known as: LNP* VERTON* Compound RFL-8029 Product reorder name: RVL29XXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.48 | % | |
| Flow : 24 hr | 0.13 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.46 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 231 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 13600 | MPa | |
| 60°C | 11700 | MPa | |
| 100°C | 10500 | MPa | |
| 150°C | 9000 | MPa | |
| 200°C | 8900 | MPa | |
| Flexural Stress | ISO 178 | ||
| -- | 361 | MPa | |
| 60°C | 300 | MPa | |
| 100°C | 256 | MPa | |
| 150°C | 204 | MPa | |
| 200°C | 162 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.39 | ||
| vs. Itself - Static | 0.40 | ||
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 3.2 | % | |
| 60°C | 3.6 | % | |
| 100°C | 3.2 | % | |
| 150°C | 3.5 | % | |
| 200°C | 2.7 | % | |
| Wear Factor - Washer | 21.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C 3 | 28 | kJ/m² | |
| 23°C 4 | 30 | kJ/m² | |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -40°C | 74 | kJ/m² | |
| 23°C | 82 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 258 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.9E-5 | cm/cm/°C | |
| Specific Heat | 1480 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.27 | W/m/K | ASTM D5930 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*3 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4603 HI | RTP Company | SPS | RTP |
| Ravamid® B MF30 T | Ravago Group | Nylon 6 | Ravamid® |
| 3M™ Dyneon™ Fluoroplastic FEP 6301Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Eltex® PF6140AA | INEOS Olefins & Polymers Europe | PE Copolymer | Eltex® |
| RTP ESD 4485 | RTP Company | Nylon, Unspecified | RTP |