Sindustris PBT LW5304F
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7yBu8c_Sindustris-PBT-LW5304F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT LW5304F is a Polycarbonate + PBT (PC+PBT) material filled with 10% glass fiber. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PBT LW5304F are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 118 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 7350 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 190 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 200 | °C | |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 250 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 245 to 255 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 128/2 GL | A. Schulman Europe | ABS | POLYMAN® |
| Vistek 1863 U | Visual Polymer Technologies, LLC | TP, Unspecified | Vistek |
| APEL™ APL8008T | Mitsui Chemicals America, Inc. | COC | APEL™ |
| Sarlink® TPV 2455-1 | Teknor Apex Company | TPV | Sarlink® TPV |
| SABIC® LDPE PCG09 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |