WELLAMID Nylon 6000/42 GVS 10/15 HWCP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7yAy9R_WELLAMIDNylon600042GVS1015HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6000/42 GVS 10/15 HWCP is a polyamide 6 (nylon 6) material, which contains 10% glass fiber reinforcement and 15% glass beads. This product is available in Europe,. The main features of WELLAMID Nylon 6000/42 GVS 10/15 HWCP are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Transverse flow : 4.00mm | 0.70 | -- | % | |
| Flow : 4.00mm | 0.50 | -- | % | |
| Water Absorption (Saturation, 23°C) | 1.8 - 2.3 | -- | % | DIN 53495 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5000 | 2900 | MPa | ISO 527-2 |
| Tensile Stress | 95.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | 15 | % | ISO 527-2/5 |
| Flexural Modulus | 4000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 25 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | 95 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 160 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 185 | -- | °C | ISO 306/B50 |
| Melting Temperature | 215 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 3.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.070 | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | HB | UL 94 | |
| 3.2 mm | HB | HB | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 70 - 100 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 7051SS | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Shandong PP PRM4201 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Telcar® GS2502 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Geon™ Specialty Suspension CG E 44 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |