EL-Pro™ P607F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7y5uO7_EL-Pro-P607F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Pro™ P607F is a homopolymer polypropylene resin without slip and antiblocking agent suitable for cast film application as a core layer of a co-extrusion film or a monolayer film requiring high film stiffness and high clarity. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1610 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 20 µm | 510 | MPa | |
| 2% Secant, TD : 20 µm | 382 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 28.4 | MPa | |
| TD : Yield, 20 µm | 22.6 | MPa | |
| MD : Break, 20 µm | 36.3 | MPa | |
| TD : Break, 20 µm | 8.83 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 470 | % | |
| TD : Break, 20 µm | 20 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 154 | °C | ASTM D1525 |
| Melting Temperature | 162 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20.0 µm) | 84 | ASTM D2457 | |
| Haze (20.0 µm) | 1.3 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP H1500 | LG Chem Ltd. | PP Homopolymer | SEETEC PP |
| Zhongfa PC/ABS CL-90 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC+ABS | Zhongfa |
| Electrafil® J-1/CF/20 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| TECHNYL® A 218 V15 BLACK 51 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Sylvin 8493-78 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |