Ultramid® A3WG6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7xSttX_Ultramid-A3WG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3WG6 is a 30% glass fiber reinforced and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation | 5.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 7200 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 186 | -- | MPa | ASTM D638 |
| Break, 23°C | 190 | 130 | MPa | ISO 527-2 |
| Break, 121°C | 93.0 | 74.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 8480 | -- | MPa | ASTM D790 |
| 23°C | 8600 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 13 | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 85 | 100 | kJ/m² | |
| Notched Izod Impact | ||||
| -40°C | 91 | -- | J/m | ASTM D256 |
| 23°C | 110 | -- | J/m | ASTM D256 |
| 23°C | 12 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 1.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.710 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 5.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.014 | 0.23 | ||
| 1 MHz | 0.014 | 0.30 | ||
| Comparative Tracking Index | 450 | 450 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G2043-00 | RheTech, Inc. | Nylon 66 | Rhelon |
| Sindustris PP H7631 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Arak LLDPE HD5050EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| DINALON® A1S25 MI | Grupo Repol | Nylon 66 | DINALON® |
| Sylvin 5145-75 Red 6193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |