Triapol® Blends F3 K0595 VRM0242 BS306
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Triapol® Blends |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7xQexi_Triapol-Blends-F3-K0595-VRM0242-BS306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polymer blend PC / ABS in red color, mainly characterized by its resistance to impact and temperature, have good resistance chemical. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ASTM D638 |
| Tensile Strength 1 | 58.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Strength | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 71 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 2 |
| Melting Temperature | 225 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 23 mm/min |
| 2 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P1187 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MAXTEL® 600T15IMUV | MRC Polymers, Inc. | TPO | MAXTEL® |
| RTP 2302 A | RTP Company | PUR, Unspecified | RTP |
| Wellamid® MRGF3822-BK | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| CALP FR200GF | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |