| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7wgzag_AEI-SX744-CM488.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Silane crosslinkable medium density polyethylene for high temperature pressure pipes Material SX744 is a silane grafted MDPE compound, curable by exposure to moist conditions, and possessing good extrusion properties at high output rates. The graft component SX744 is mixed with a crosslinking catalyst masterbatch CM488 generally in the ratio 95:5. The highly crosslinked materials produced by the two-component system possess excellent impact strength, ESCR, creep and internal pressure resistance under ambient and elevated temperature conditions. These materials have been formulated for hot and cold water pressure pipes and are easily extrudable on conventional polyethylene extrusion lines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | BS 2782 620A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | Internal method |
| Gel Content | 72 | % | ASTM D2765 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811-2-1 | ||
| Elongation under load, 20N/cm² : 200°C | 55 | % | IEC 60811-2-1 |
| Permanent elongation after cooling | 0.0 | % | IEC 60811-2-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 | °C | |
| Extruder Screw L/D Ratio | 20.0:1 to 25.0:1 | ||
| Extruder Screw Compression Ratio | 2.5:1 to 3.0:1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant | 650 | MPa | BS 2782 320A |
| Tensile Stress | 24.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 550 | % | IEC 60811-1-1 |
| Additional Information |
|---|
| Crosslinking or cure: If properly processed the material has the capacity of crosslinking under ambient conditions.Should accelerated cure times be required, then any of the following methods may be employed. Immersion in water at 80°C Flushing with water at 80°C Exposure to steam at 90°C (as in a sauna) |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 175 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 318CN | SABIC Americas, Inc. | LLDPE | SABIC® LLDPE |
| Staramide BG6U | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| TRIBOCOMP® PA66 CF30 TS12 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| EPIMIX PBT GFR 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| KEBAFORM® C 130 LS weiß | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |