LNP™ LUBRICOMP™ KP004 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7wVvLG_LNPLUBRICOMPKP004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KP004 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Also known as: LNP* LUBRICOMP* Compound KL-4540 Product reorder name: KP004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Across Flow (24 hr) | 2.1 - 2.9 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 39.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 15 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Flexural Stress | 47.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.25 | ASTM D3702 Modified | |
| With Self-Static | 0.14 | ASTM D3702 Modified | |
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 79.0 | °C | ISO 75-2/Af |
| CLTE - Flow (23 to 60°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 9020 HS | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
| VITAMIDE® BF30GY6699 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| LACEA® H-100J (Unstretched) | Mitsui Chemicals, Inc. | PLA | LACEA® |
| Karina BLACK COLOR CONCENTRATE 48/1-GI (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina NATURAL PVC COMPOUND 70900-25/ 1-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |