PENTAMID A GV50 H natur
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7wUvOc_PENTAMID-A-GV50-H-natur.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, 50% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.40 | -- | % | |
| Flow | 0.25 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 260 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 15500 | 12600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 225 | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 14000 | -- | MPa | ISO 178 |
| Flexural Stress | 330 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | |
| 23°C | 18 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | -- | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength (1.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | -- | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA66, MHR, 14-160, GF50 | PA66, MHR, 14-160, GF50 | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 275 to 300 | °C | |
| Middle Temperature | 290 to 305 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Processing (Melt) Temp | 295 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 90.0 | MPa | |
| Holding Pressure | 54.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® X681 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Hax™ CAT 111 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Innothane® IE-6000 | Innovative Polymers, Inc. | TSU | Innothane® |
| Jam HDPE HM8355 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Polipom 100D | Poliblend S.p.a. | Acetal (POM) Homopolymer | Polipom |