RTP 3483-3 TFE 15
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7vif9w_RTP-3483-3-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 26900 | MPa | ASTM D638 |
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.90 | % | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Volume Resistivity, ASTM D257: 1E6-1E9 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 335 - 354 | °C | |
| Middle Temperature | 335 - 354 | °C | |
| Front Temperature | 335 - 354 | °C | |
| Nozzle Temperature | 343 - 379 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 103 - 138 | MPa | |
| Clamp Tonnage | 5.5 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell PE 1840 H | LyondellBasell Industries | LDPE | Purell |
| Toler PP 9038N | Toler Chemical, Inc | PP Homopolymer | Toler PP |
| KumhoSunny PC HCG2530MP | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| POLYCOMPO PP S115 | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| POLYfill PPHC TS15020 | Polykemi AB | PP, Unspecified | POLYfill |