| LEXAN 4701R is a copolymer of polyphtalate carbonate resin for applications requiring high heat resistance. This grade has higher heat properties compared to LEXAN 4501. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.90 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 127 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 46 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -30°C | 11 | kJ/m² | ISO 180/1A |
| 23°C | 35 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 165 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 150 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ISO 306/A50 |
| -- | 175 | °C | ISO 306/B50 |
| -- | 170 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (23 to 80°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.026 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 125 - 135 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 310 - 330 | °C | |
| Front Temperature | 320 - 340 | °C | |
| Nozzle Temperature | 320 - 340 | °C | |
| Processing (Melt) Temp | 325 - 360 | °C | |
| Mold Temperature | 100 - 125 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*3 |
| 6 . | 80*10*3 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E580 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Cellophane™ 325P32 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| PEARLCOAT® 127K | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLCOAT® |
| Sylvin 6930X06 Brown 7454 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® DP 2131/20 H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |