COSMOTHENE® EVA K3212
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOTHENE® EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7uLKwC_COSMOTHENE-EVA-K3212.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOTHENE EVA is produced by the latest autoclave process technology licensed by Sumitomo Chemical Co. Japan. COSMOTHENE EVA have good processability, tough, elastic good ESCR and good low temperature resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | > 300 | hr | ASTM D1693 |
| Vinyl Acetate Content | 21.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 28 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Apparent Bending Modulus | 29.4 | MPa | ASTM D747 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 58.0 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6050NC | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| NYCOA Polyamide 2137 | Nycoa (Nylon Corporation of America) | Nylon Copolymer | NYCOA Polyamide |
| Axiall PVC 7751 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Genestar™ N1002A-M41 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Plaslube® POM HO GF20 TL20 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |