VESTAMID® D DX9305
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® D |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7sUd1E_VESTAMID-D-DX9305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characterization: heat- and light-stabilized Applications: tubing systems subjected to higher temperatures, e.g., hydraulic clutch lines Its advantages over PA 12 exhibit in the
The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 1.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.7 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2250 | 1500 | MPa | ISO 527-2/1A |
| Tensile Stress (Yield) | 60.0 | 49.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 4.3 | 18 | % | |
| Break | > 50 | > 50 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C, Complete Break | 6.0 | 7.0 | kJ/m² | |
| 23°C, Complete Break | 6.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed 2 | 185 | -- | °C | ISO 75-2/B |
| 0.45 MPa, Unannealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 3 | 70.0 | -- | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 185 | -- | °C | ISO 306/B |
| Melting Temperature 4 | 213 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.4E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 23 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.30 | -- | ||
| 1 MHz | 3.30 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.055 | -- | ||
| 1 MHz | 0.032 | -- | ||
| Comparative Tracking Index 5(Solution A) | > 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Electrolytical Corrosion | AN 1,2 | -- | IEC 60426 | |
| ISO Shortname | PA612, EHL, 22-020 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | measured at specimen 60x60x2mm |
| 2 . | after conditioning at 180 °C / 60 min |
| 3 . | after conditioning at 180 °C / 60 min |
| 4 . | 2nd Heating |
| 5 . | 50 drops Value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive SE900-5 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| NEXT SIGNATURE PPH T40-100 | NEXT Specialty Resins, Inc. | PP Homopolymer | NEXT SIGNATURE |
| Generic Epoxy - Mineral | Generic | Epoxy | Generic |
| PETILEN F5-21T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |
| OTECH ALLOY NT1000-80 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |