Dialon 3035
| Category: | PC , Polycarbonate |
| Manufacturer: | DTR S.r.l. (Develop Thermoplastic Resins) |
| Trademark: | Dialon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7ruCUK_Dialon-3035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dialon 3035 is a Polycarbonate (PC) material. It is available in Europe. Important attributes of Dialon 3035 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 33 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ M2400NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Sindustris PC SF1010 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| TEKNIFLEX® VPOA10300 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| Nypol® PA B3 HL UV NTLA010 NT373 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| ISOTHANE® 8303 | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU, Unspecified | ISOTHANE® |