Hyundai EP PA66 LD900
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7rqrzn_Hyundai-EP-PA66-LD900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Base Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.3 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 78.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2750 | MPa | ASTM D790 |
| Flexural Strength | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Melting Temperature | 265 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 3.5 | kV/mm | ASTM D149 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-Comp™ PPHGF40-E | Southland Polymers | PP Homopolymer | Pro-Comp™ |
| WELLAMID Nylon 6600 GS 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| PENTAMID A GV30 HYD schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| PLUSTEK PA303G33 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Sylvin 4200-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |