Deltron 1150
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Shanghai Lin Gen Rubber Materials Co., Ltd. |
| Trademark: | Deltron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7qhC6l_Deltron1150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Deltron 1150 is a polyphenylene sulfide (PPS) material, which contains filler. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of the Deltron 1150 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 - 0.70 | % | |
| Water Absorption (Equilibrium) | 0.020 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 185 | MPa | |
| Tensile Elongation (Break) | 2.8 | % | |
| Flexural Modulus | 16000 | MPa | |
| Flexural Strength | 300 | MPa | |
| Compressive Strength | 154 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Notched Izod Impact | 16.0 | kJ/m² |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 268 | °C | |
| Melting Temperature | 288 | °C | |
| CLTE - Flow | 1.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 2.2E+15 | ohms | |
| Volume Resistivity | 8.0E+16 | ohms·cm | |
| Dielectric Strength | 18 | kV/mm | |
| Dielectric Constant (1 MHz) | 3.00 |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flame Rating (2.0 mm) | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 300 - 330 | °C | |
| Mold Temperature | 100 - 140 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 60.0 - 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210LW | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Synres-Almoco SI 4554 | Synres-Almoco BV | Silicone | Synres-Almoco |
| UBE Polyethylene J1019 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Fainplast PVC RK 810 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| LGE 422 LD | LG Polymers India Pvt. Ltd. | PS (EPS) | LGE |