Order Products : sales@su-jiao.com
Kangxi® FRABSMIV-0
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Wuxi Kangxi Plastics Technology Co.,Ltd. |
| Trademark: | Kangxi® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7pkP62_KangxiFRABSMIV0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kangxi®FRABSMIV-0 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in the Asia-Pacific region. Kangxi®FRABSMIV-0 application areas include electrical appliances, automobile industry and sporting goods. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 15 | % | ASTM D638 |
| Flexural Modulus 4 | 2150 | MPa | ASTM D790 |
| Flexural Strength 5 | 55.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 80.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | V-0 | UL 94 | |
| 3.2 mm | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weather Resistance - 24 hr (23°C) | 0.040 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 - 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 230 | °C | |
| Middle Temperature | 180 - 230 | °C | |
| Front Temperature | 180 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 30 - 60 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® PJ5300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Sumitomo PP Y101 | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| WanBlend® WHT-THF9485T2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Clariant ABS ABS5400 | Clariant Corporation | ABS | Clariant ABS |
| Sylvin 29168-65 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |