LNP™ LUBRICOMP™ DFL28 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7pWlYO_LNPLUBRICOMPDFL28compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DFL-4028 Product reorder name: DFL28 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.51 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.21 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13800 | MPa | ASTM D638 |
| -- | 12900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 149 | MPa | ASTM D638 |
| Yield | 145 | MPa | ISO 527-2 |
| Fracture | 149 | MPa | ASTM D638 |
| Fracture | 145 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 2.2 | % | ASTM D638, ISO 527-2 |
| Fracture | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 11700 | MPa | ASTM D790 |
| -- | 11800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 207 | MPa | ASTM D790 |
| -- | 216 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.53 | ASTM D3702 Modified | |
| With Self-Static | 0.53 | ASTM D3702 Modified | |
| Wear Factor - Washer | 129 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 890 | J/m | ASTM D4812 |
| 23°C 3 | 57 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 22.7 | J | ASTM D3763 |
| -- | 5.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 145 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 140 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 142 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M8147 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MIDILENA III PPJ700 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Niche PA66GF13N | Niche Polymer, LLC | Nylon 66 | Niche |
| ACCUTECH™ HP0336T30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Celstran® PP-GF40-04 Natural | Celanese Corporation | PP, Unspecified | Celstran® |