Edistir® RK 451G
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7pSzgR_Edistir-RK-451G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UL94 V-0, polybromobiphenylether (PBBE) free, flame retarded, high impact polystyrene. This grade combines medium flow, heat resistance and good light stability for injection moulding of technical parts. Designation: Thermoplastics ISO 2897-PS-I,MF,O88-06-04-18 Applications Printers and copiers, ventilators, TV back covers, business machines, monitor cabinets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1950 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 23.0 | MPa | |
| Break | 22.0 | MPa | |
| Tensile Strain (Break) | 50 | % | ISO 527-2/50 |
| Flexural Stress 1 | 31.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 80 | J/m | ISO 180/4A |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 4.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, All Colors | V-0 | ||
| 4.00 mm, All Colors, foamed at density 0.96 to 1.2 g/cm³ | 5VA | ||
| 6.00 mm, All Colors, foamed at density 0.86 to1.16 g/cm³ | 5VA | ||
| Glow Wire Ignition Temperature (1.60 mm) | 850 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastics ISO 2897-PS-I,M,088-06-04-18 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 105 CC TFE 15 | RTP Company | PP, Unspecified | RTP |
| Trademark PP PPR3500MA | Trademark Plastics Corporation | PP Random Copolymer | Trademark PP |
| TOTAL Polypropylene PPC 7612 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| ALTECH® PA66 A 2015/109 GF15 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Geon™ Vinyl Rigid Extrusion 06935L | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |