LNP™ LUBRICOMP™ 9X98026 compound
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7notTR_LNP-LUBRICOMP-9X98026-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP 9X98026 is a compound based on PA4.6 resin containing Barium Sulfate, PTFE and Carbon Fiber Also known as: LNP* LUBRICOMP* Compound PDX-STN-98026 Product reorder name: 9X98026 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 159 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 14200 | MPa | ISO 178 |
| Flexural Stress | 207 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 1.8 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 19 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 289 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 281 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 310 to 321 | °C | |
| Mold Temperature | 82.2 to 121 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLLAMID B 2700 FV 50 | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| APEX® 94-A0098A-80 | Teknor Apex Company | PVC, Flexible | APEX® |
| DESOX™ DSC401 | DESCO Co., Ltd. | PBT | DESOX™ |
| Dugdale PVC Rigid Clear Extrusion - Blue Tint Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Petrothene® LT570401 | LyondellBasell Industries | HDPE | Petrothene® |