Kangxi® FRPA6-30GF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wuxi Kangxi Plastics Technology Co.,Ltd. |
| Trademark: | Kangxi® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7nLEsI_KangxiFRPA630GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kangxi®FRPA6-30GF is a polyamide 6 (nylon 6) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 135 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus 4 | 8000 | MPa | ASTM D790 |
| Flexural Strength 5 | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 218 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 215 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | V-0 | UL 94 | |
| 3.2 mm | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weather Resistance - 24 hr (23°C) | 0.60 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 30 - 60 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4150R50 | Technical Polymers, LLC | PPS | Thermec™ |
| Toughblend® PA6-1300 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| WPP PP PPC5GF2-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| UBE Nylon 1013 IU50 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| ULTEM™ HU2100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |