Fiberfil®PP-60/TC/24/D/HS is a polypropylene homopolymer (PP Homopoly) material, which contains talc filler. This product is available in North America,. Fiberfil®The main features of PP-60/TC/24/D/HS are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.90 - 1.0 | % | ASTM D955 |
| 6.35 mm | 1.1 - 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2900 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium to Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PP CONC 36 NAT S | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| Sup-tech B9260 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| Abstron SE45 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Generic PBT - Glass Bead\Glass Fiber | Generic | PBT | Generic |
| MTEGRITY™ LLDPE LL204MM | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |