SHINSTRA AMG40TKB (PA6)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Shinil Chemical Industry Co., Ltd. |
| Trademark: | SHINSTRA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7mKbtw_SHINSTRAAMG40TKBPA6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SHINSTRA is our flagship product - provide improved modulus, impact resistance and heat resistance which are the weak points of plastic materials. Generally, SHINSTRA satisfy requirements by customizing (1) impact resistance, (2) scratch resistance, (3) abrasion, (4) chemical resistance, (5) processability and (6) heat resistance. In addition to the excellent products, we are offering total solution optimizing product designand customer's process lines through Computer Aided Engineering (CAE). SHINSTRA can be produced with PC, HIPS, PE, PP, PA-6 and PA-6,6 in our proprietary dispersion technology and used in many applications such as exterior and interior auto parts, home appliance and construction materials. APPLICATION: inside door handle |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 - 0.60 | % | Internal method |
| Moisture Content | 0.040 | % | ISO 15512 |
| Ash Content | 37 - 43 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ISO 527-2/5 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 2 | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | 1.0E+14 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 240 - 270 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10°C/min |
| 3 . | 23°C/50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melinex® 990 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| VITAMIDE® AR37BK9024 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| YUPLENE® BX3800 | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| Hostacom M2 N01 L304698 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Karina IVORY PVC COMPOUND -E 880-35/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |