Sumikon® PM-6280
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7lIOru_SumikonPM6280.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON PM-6280 Type Black is a Short Glass fiber molding compound based on Phenolic Novolac polymer. It is supplied in the form of Granular/Molding Powder for Molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.94 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.25 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.040 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 106 | MPa | JIS K6911 |
| Flexural Modulus | 21200 | MPa | JIS K6911 |
| Flexural Strength | 244 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.6 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | JIS K6911 | ||
| -- 1 | 3.0E+10 | ohms | JIS K6911 |
| -- 2 | 3.0E+9 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | As molded |
| 2 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufprene™ A | AKelastomers | SBS | Tufprene™ |
| Garaflex™ E 89-086-C3 NAT NF LCF-R | AlphaGary | TPE | Garaflex™ E |
| HANWHA LDPE 5318 | Hanwha Chemical | LDPE | HANWHA LDPE |
| ICORENE® N2309 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| LEXAN™ EX1632T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |